Experimental Evaluation of the Performance of Fresh Nano Zeolite as an Oil Well Cement Additive

Received: 24 January 2021     Accepted: 6 February 2021     Published: 10 February 2021
Views:       Downloads:
Abstract

Cementing oil and gas wells require materials that, not only meet performance standards but also fairly different from those encountered in conventional processes. The search for alternative materials for cementing oil wells has increased worldwide. It is desirable that these alternative materials make cement sheath stronger, durable, flexible, cost-effective and more resistant to shocks. This research aimed at evaluating the performance of fresh nano zeolite as an additive for shallow oil well cementing operations. Laboratory tests were conducted on a base cement slurry mixed with different concentrations of fresh nano zeolite from 1% bwoc to 3% bwoc at a Bottomhole Circulating Temperature (BHCT) of 80°F (27°C) to determine physical properties such as compressive strength, thickening time, rheology, free fluid, and fluid loss. The results showed that the compressive strength of the cement slurries improved significantly at 12 hours than 24 hours curing period at 87°F (31°C). As the concentration of fresh nano zeolite increases less time was required to reach 50 psi, 100 psi and most importantly 500 psi which is needed to resume drilling operations. An increase in concentration of fresh nano zeolite at 80°F (27°C) resulted in an increase in the thickening time of all the cement slurries. This shows that fresh nano zeolite has a high retardation effect. Generally, the addition of fresh nano zeolite from 1% bwoc to 3% bwoc improved the carrying capacity of all the cement slurries. Test results also showed that increasing the fresh nano zeolite concentrations resulted in a decrease in rheological values which is a characteristic of a dispersant. Plastic viscosity values were observed to have an increasing trend generally with an increasing concentration of fresh nano zeolites. All the cement slurries were below 100 cP and therefore pumpable. The addition of fresh nano zeolite to the base cement slurry increased the free fluid of the cement slurries. The fresh nano zeolite didn’t have any effect on fluid loss and therefore does not exhibit characteristics of a fluid loss agent.

Published in Petroleum Science and Engineering (Volume 5, Issue 1)
DOI 10.11648/j.pse.20210501.11
Page(s) 1-12
Creative Commons

This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.

Copyright

Copyright © The Author(s), 2021. Published by Science Publishing Group

Keywords

Compressive Strength, Fluid Loss, Free Fluid, Fresh Nano Zeolite, Thickening Time

References
[1] Hodne, H. (2007), “Rheological Performance of Cementitious Materials used in Well Cementing”, PhD Thesis, University of Stavanger, Stavanger, Norway, 8 p.
[2] Ridha, S., Irawan, S., Ariwahjoedi, B. and Jasamai, M. (2010), “Conductivity Dispersion Characteristic of Oilwell Cement Slurry during Early Hydration”, International Journal of Engineering and Technology, Vol. 10, No. 6, pp. 121–124.
[3] Ershadi, V., Ebadi, T., Rabani, A. R., Ershadi, L. and Soltanian, H. (2011), “Reduction of Set Cement Permeability in Oil Well to Decrease the Pollution of Receptive Environment using Spherical Nanosilica, 2nd International Conference on Environmental Science and Technology, IPCBEE, Singapore, Vol. 6, pp. 101–104.
[4] Pourafshary, P., Azimipour, S. S., Motamedi, P., Samet, M., Taheri, S. A. and Bargozin, H. P. (2009), “Priority Assessment of Investment in Development of Nanotechnology in Upstream Petroleum Industry” Society of Petroleum Engineers Saudia Arabia Section Technical Symposium, SPE 126101, AlKhobar, Saudi Arabia, pp. 1–11.
[5] Nelson, E. B., Baret, J. F. and Michaux, M. (1990), “Cement Additives and Mechanism of Action”, In Well Cementing, E. B. Nelson (Ed.), Elsevier Science Publishers, Amsterdam, pp. 3-37.
[6] Boni-Bediako, E., Joel, O. F. and Ofori-Sarpong, G. (2016), “Oil Well Cement Additives: A Review of the Common Types”, Oil and Gas Research, Vol. 2, No. 1, pp. 1-7.
[7] Ahmadi, B. and Shekarchi, M. (2010), “Use of Natural Zeolite as a Supplementary Cementitious Material”, Cement and Concrete Composites, Vol. 32, No. 2, pp. 134-141.
[8] Luke, K., Reddy, B. R, Fitzgerald, R. M., Zamora, F., Fyten, G. C, Rispler, K. A, Getzlaf, D. A, Gray, D. W. and Dealy, S. T. (2004), “Zeolite Containing Cement Composition”, US Patent Application Publication, No. 0112600 2, 39 pp.
[9] Baig, M. T. (2017), “Evaluation of Nano Zeolite as an Additive for Oil-Well Cementing”, Unpublished MSc Thesis, King Fahd University of Petroleum and Minerals, Dhahran, Saudi Arabia, 143 pp.
[10] Byrappa, K. and Yoshimura, M. (2001), “Hydrothermal Technology Principles and Applications”, Handbook of Hydrothermal Technology, pp. 1-52.
[11] Tsitsishvili, G. V., Skhirtladze, N. S., Andronikashvili, T. G., Tsitsishvili, V. G. and Dolidze, A. V. (1999), “Natural Zeolites of Georgia: Occurrences, Properties, and aAplication”, Studies in Surface Science and Catalysis, Vol. 125, pp. 715-722.
[12] Nagrockiene, D. and Girskas, G. (2016), “Research into the Properties of Concrete Modified with Natural Zeolite Addition”, Construction and Building Materials, Vol. 113, pp. 964-969.
[13] Caputo, D., Liguori, B. and Colella, C. (2008), “Some Advances in Understanding the Pozzolanic Activity of Zeolites: The Effect of Zeolite Structure", Cement and Concrete Composites, Vol. 30, No. 5, pp. 455-462.
[14] Amarfio, E. M. (2020), “Effect of Al2O3 Nanoparticles, Fresh and Equilibrium Zeolite, on the Rheological Behaviour of WBM Systems at the High Temperature”, PhD Seminar Presentation, University of Mines and Technology, Tarkwa, Ghana, 30 pp.
[15] Huwel, J. P. E., Faustino, V. and Roberts, R. (2014), “Cement Compressive Strength Development Drastically Affected by Testing Procedure”, Proceedings of American Association of Drilling Engineers Fluid Conference and Exhibition, pp. 1-5.
[16] Anon (1997), American Petroleum Institute (API) Recommended Practice 10B for Testing Well Cements, American Petroleum Institute, Washington D. C., USA, 134 pp.
[17] Anon (2013), American National Standard Institute/American Petroleum Institute (ANSI/API) Specification 10A for Cements and Materials for Well Cementing, API Publication Services, Washington D. C., 38 pp.
[18] Abbas, G. Irawan, S. Kumar, S. Memon, R. K. and Khalwar, S. A. (2014), “Characteristics of Oil Well Cement Slurry using Hydroxypropylmethylcellulose”, Journal of Applied Sciences, 14: pp. 1154–1160.
[19] Broni-Bediako, E. Ofori-Sarpong, G. and Joel. O. F. (2015), Comparative Study of Local Cements with Imported Class ‘G’ Cement at Different Temperatures of Oil Well Cementing Operations in Ghana, Journal of Petroleum and Environmental Biotechnology, Vol. 6, No. 4, pp. 1–7.
[20] Broni-Bediako, E. and Amorin, R. (2018), “Enhancing the Performance of Local Cement as an Alternative for Oil and Gas Well Cementing Operation”, Petroleum and Coal, Vol. 60, No. 5, pp. 977–984.
[21] De Andrade, J. and Sangesland, S. (2016), “Cement Sheath Failure Mechanisms: Numerical Estimates to Design for Long-term Well Integrity”, Journal of Petroleum Science and Engineering, Vol. 147, pp. 682-698.
[22] Sze, W. H. and Kadir, A. A. (2011), “The Potential of Lawin Tuff for Generating a Portland Fly Ash Cement to be used in Oil Well Cementing”, International Journal of Engineering and Technology, Vol. 11, pp. 51–55.
[23] Kutasov, I. M. and Eppelbaum, L. V. (2014), “Temperature Regime of Boreholes: Cementing of Production Liners”, Proceedings of the 2014 Stanford Geothermal Workshop, pp. 1-5.
[24] Shuker, M. T, Memon, K. R., Tunio, S. Q. and Memon, M. K. (2014), “Laboratory Investigation on Performance of Cement Using Different Additives Schemes to Improve Early Age Compressive Strength”, Research Journal of Applied Sciences, Engineering and Technology, Vol. 7 (11), pp. 2298–2305.
[25] Murtaza, M., Mahmoud, M. and Tariq, Z. (2020), “Experimental Investigation of a Novel, Efficient, and Sustainable Hybrid Silicate System in Oil and Gas Well Cementing”, Energy and Fuels, Vol. 34, No. 6, pp. 7388-7396.
[26] Labibzadeh, M., Zahabizadeh, B. and Khajehdezfuly, A. (2010), “Early-age Compressive Strength Assessment of Oil well Class G Cement due to Borehole Pressure and Temperature Changes”, Journal of American Science, Vol. 6, No. 7, pp. 38-47.
[27] Alp, B. and Akin, S. (2013), “Utilization of Supplementary Cementitious materials in geothermal Well Cementing”, Proceedings of Thirty-Eighth Workshop on Geothermal Reservoir Engineering, pp. 1-7.
[28] Roshan, H. and Asef, M. R. (2010), “Characteristics of Oilwell Cement Slurry using CMC", Drilling and Completion, Vol. 25, No. 3, pp. 328-335.
[29] Broni-Bediako, E., Joel, O. F. and Ofori-Sarpong, G. (2016), “Oil Well Cement Additives: A Review of the Common Types”, Oil and Gas Research, Vol. 2, No. 1, pp. 1-7.
[30] Bett, E. K. (2010), “Geothermal Well Cementing, Materials and Placement Techniques”, Geothermal Training Programme Report, No. 10, pp. 99–130.
[31] Azar, J. J. and Samuel, G. R. (2007), “Drilling Engineering”, PennWell Corporation, Tulsa, OK, USA, 438 pp.
[32] Salehi, R. and Paiaman, A. M. (2009), “A Novel Cement Slurry Design Applicable to Horizontal Well Conditions”, Petroleum and Coal; Vol. 51, No. 4, pp. 270-276.
[33] Magzoub, M., Mahmoud, M., Nasser, M., Hussein, I., Elkatatny, S. and Sultan, A. (2019), “Thermochemical Upgrading of Calcium Bentonite for Drilling Fluid Applications”, Journal of Energy Resources Technology, Vol. 141, No. 4. pp. 1–25.
[34] Luo, J., Zhang, C., Duan, Z., Wang, B., Li, Q., Chung, K. L., Zhang, J. and Chen, S. (2018), “Influences of Multi-walled Carbon Nanotube (MCNT) Fraction, Moisture, Stress/Strain Level on the Electrical Properties of MCNT Cement-based Composites”, Sensors and Actuators A: Physical, Vol. 280, pp. 413-421.
[35] Elkatatny, S., Gajbhiye, R., Ahmed, A. and Mahmoud, A. A. (2020), “Enhancing the Cement Quality using Polypropylene Fiber”, Journal of Petroleum Exploration and Production Technology, Vol. 10, No. 3, pp. 1097-1107.
Cite This Article
  • APA Style

    Eric Broni-Bediako, Fulgence Maal-Ire Naatu. (2021). Experimental Evaluation of the Performance of Fresh Nano Zeolite as an Oil Well Cement Additive. Petroleum Science and Engineering, 5(1), 1-12. https://doi.org/10.11648/j.pse.20210501.11

    Copy | Download

    ACS Style

    Eric Broni-Bediako; Fulgence Maal-Ire Naatu. Experimental Evaluation of the Performance of Fresh Nano Zeolite as an Oil Well Cement Additive. Pet. Sci. Eng. 2021, 5(1), 1-12. doi: 10.11648/j.pse.20210501.11

    Copy | Download

    AMA Style

    Eric Broni-Bediako, Fulgence Maal-Ire Naatu. Experimental Evaluation of the Performance of Fresh Nano Zeolite as an Oil Well Cement Additive. Pet Sci Eng. 2021;5(1):1-12. doi: 10.11648/j.pse.20210501.11

    Copy | Download

  • @article{10.11648/j.pse.20210501.11,
      author = {Eric Broni-Bediako and Fulgence Maal-Ire Naatu},
      title = {Experimental Evaluation of the Performance of Fresh Nano Zeolite as an Oil Well Cement Additive},
      journal = {Petroleum Science and Engineering},
      volume = {5},
      number = {1},
      pages = {1-12},
      doi = {10.11648/j.pse.20210501.11},
      url = {https://doi.org/10.11648/j.pse.20210501.11},
      eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.pse.20210501.11},
      abstract = {Cementing oil and gas wells require materials that, not only meet performance standards but also fairly different from those encountered in conventional processes. The search for alternative materials for cementing oil wells has increased worldwide. It is desirable that these alternative materials make cement sheath stronger, durable, flexible, cost-effective and more resistant to shocks. This research aimed at evaluating the performance of fresh nano zeolite as an additive for shallow oil well cementing operations. Laboratory tests were conducted on a base cement slurry mixed with different concentrations of fresh nano zeolite from 1% bwoc to 3% bwoc at a Bottomhole Circulating Temperature (BHCT) of 80°F (27°C) to determine physical properties such as compressive strength, thickening time, rheology, free fluid, and fluid loss. The results showed that the compressive strength of the cement slurries improved significantly at 12 hours than 24 hours curing period at 87°F (31°C). As the concentration of fresh nano zeolite increases less time was required to reach 50 psi, 100 psi and most importantly 500 psi which is needed to resume drilling operations. An increase in concentration of fresh nano zeolite at 80°F (27°C) resulted in an increase in the thickening time of all the cement slurries. This shows that fresh nano zeolite has a high retardation effect. Generally, the addition of fresh nano zeolite from 1% bwoc to 3% bwoc improved the carrying capacity of all the cement slurries. Test results also showed that increasing the fresh nano zeolite concentrations resulted in a decrease in rheological values which is a characteristic of a dispersant. Plastic viscosity values were observed to have an increasing trend generally with an increasing concentration of fresh nano zeolites. All the cement slurries were below 100 cP and therefore pumpable. The addition of fresh nano zeolite to the base cement slurry increased the free fluid of the cement slurries. The fresh nano zeolite didn’t have any effect on fluid loss and therefore does not exhibit characteristics of a fluid loss agent.},
     year = {2021}
    }
    

    Copy | Download

  • TY  - JOUR
    T1  - Experimental Evaluation of the Performance of Fresh Nano Zeolite as an Oil Well Cement Additive
    AU  - Eric Broni-Bediako
    AU  - Fulgence Maal-Ire Naatu
    Y1  - 2021/02/10
    PY  - 2021
    N1  - https://doi.org/10.11648/j.pse.20210501.11
    DO  - 10.11648/j.pse.20210501.11
    T2  - Petroleum Science and Engineering
    JF  - Petroleum Science and Engineering
    JO  - Petroleum Science and Engineering
    SP  - 1
    EP  - 12
    PB  - Science Publishing Group
    SN  - 2640-4516
    UR  - https://doi.org/10.11648/j.pse.20210501.11
    AB  - Cementing oil and gas wells require materials that, not only meet performance standards but also fairly different from those encountered in conventional processes. The search for alternative materials for cementing oil wells has increased worldwide. It is desirable that these alternative materials make cement sheath stronger, durable, flexible, cost-effective and more resistant to shocks. This research aimed at evaluating the performance of fresh nano zeolite as an additive for shallow oil well cementing operations. Laboratory tests were conducted on a base cement slurry mixed with different concentrations of fresh nano zeolite from 1% bwoc to 3% bwoc at a Bottomhole Circulating Temperature (BHCT) of 80°F (27°C) to determine physical properties such as compressive strength, thickening time, rheology, free fluid, and fluid loss. The results showed that the compressive strength of the cement slurries improved significantly at 12 hours than 24 hours curing period at 87°F (31°C). As the concentration of fresh nano zeolite increases less time was required to reach 50 psi, 100 psi and most importantly 500 psi which is needed to resume drilling operations. An increase in concentration of fresh nano zeolite at 80°F (27°C) resulted in an increase in the thickening time of all the cement slurries. This shows that fresh nano zeolite has a high retardation effect. Generally, the addition of fresh nano zeolite from 1% bwoc to 3% bwoc improved the carrying capacity of all the cement slurries. Test results also showed that increasing the fresh nano zeolite concentrations resulted in a decrease in rheological values which is a characteristic of a dispersant. Plastic viscosity values were observed to have an increasing trend generally with an increasing concentration of fresh nano zeolites. All the cement slurries were below 100 cP and therefore pumpable. The addition of fresh nano zeolite to the base cement slurry increased the free fluid of the cement slurries. The fresh nano zeolite didn’t have any effect on fluid loss and therefore does not exhibit characteristics of a fluid loss agent.
    VL  - 5
    IS  - 1
    ER  - 

    Copy | Download

Author Information
  • Department of Petroleum and Natural Gas Engineering, School of Petroleum Studies, University of Mines and Technology (UMaT), Tarkwa, Ghana

  • Department of Petroleum and Natural Gas Engineering, School of Petroleum Studies, University of Mines and Technology (UMaT), Tarkwa, Ghana

  • Sections